“Custom Work, Quality Service”

Your Primary Choice for Polyolefin Shrink Films

ISO 9001:2015 Registered • FDA Approved • REACH Compliant

Home Products Polyolefin Shrink Films High Performance POF Film

HYF003 High Performance Polyolefin Shrink Film

is a perfect shrink film. It can help you solve nearly all shrinking difficulties. HYF003 has excellent low shrink temperature property. Its shrink temperature is nearly same as PVC shrink film's. With quick shrink, good seal strength and over 70% shrinkage, HYF003 can perform perfectly even under the worst shrink conditions. HYF003 also has low shrink force function and good hot slip property.


Features

Exceptional shrinakge under 120℃

Broad shrink temperature range, from 110℃ to 180℃

Quick shrink in 1.5 seconds

Excellent shrinkage

Low sealing temperature

Superior seal strength

Strong tear resistance

Low shrink force property

Outstanding hot slip property after shrinkage

Overlap staic sealing property

compatible for all packaging machinery.

TEST ITEM UNIT ASTM TEST TYPICAL VALUES
THICKNESS 12um 15um 19um 25um
TENSILE
Tensile Strength (MD) N/mm2 D882 76 71 71 66
Tensile Strength (TD) 66 61 61 61
Elongation (MD) % 106 106 111 111
Elongation (TD) 86 91 91 96
TEAR
MD g D1922 15.6 18.6 32.1 40.1
TD 13.6 16.6 23.6 30.1
SEAL STRENGTH
MD/Hot Wire Seal N/mm F88 0.78 0.88 1.05 1.35
TD/Hot Wire Seal 0.72 0.82 1.01 1.27
COF(film to Film)
Dynamic D1894 0.31 0.28 0.27 0.31
Static 0.32 0.29 0.28 0.32
Static (Hot Slip) @ 60℃ 0.39 0.37 0.36 0.35
OPTICS
Haze D1003 3.2 3.7 4.3 4.6
Clarity D1746 97.6 98.1 97.1 95.1
Gloss @ 45Deg D2457 86.6 84.1 82.1 80.6
BARRIER
Oxygen Transmission Rate cc/m2/day D3985 12300 11200 9400 6200
Water Vapor Transmission Rate gm/m2/day F1249 50 43 36 29
SHRINKAGE PROPERTIES MD TD MD TD
Free Shrinkage 80℃ % D2732 24 21 22 18
90℃ 30 33 28 27
100℃ 51 53 49 48
110℃ 60 61 56 57
120℃ 66 66 64 66
130℃ 71 69 69 68
Shrink Tension 90℃ Mpa D2838 1.70 1.80 1.80 1.85
100℃ 1.90 2.00 2.05 2.15
110℃ 2.05 2.10 2.25 2.30
120℃ 1.85 1.95 2.00 2.05
Note: This infor mation represents our best judgment on the work done,but the company assumes no liability whatsoever in connection with the use of infomation or findings contained herein.